Taitalac 5000W ABS Description
Taitalac 5000W is injection molding Acrylonitrile Butadiene Styrene (ABS) resin raw material, with high fluidity and high gloss characteristics. Taita 5000W is the first choice for producing high precision, complex products with high requirements on appearance quality.
| TAITALAC® ABS 5000W |
| Product information |
|
Manufacturer
|
Taita Chemical Company, Ltd.
|
|
Other Certificates
|
MSDS
|
|
Part Marking Code
|
>ABS material<
|
|
Color
|
WT Colors available
|
|
Material Shape
|
Pellets
|
|
Process
|
Injection molding ABS
|
|
FR
|
HB
|
|
Material Attribute
|
Injection grade ABS pellets
|
|
Specification
|
UL
|
|
Features
|
·High gloss ·High flow
|
|
Application
|
·Office Applications ·E & E applications ·Appliances ·Home appliances applications
·Housewares application
|
|
UL File NO
|
E50263
|
|
Physcial properties
|
Standard
|
Value
|
Unit
|
| Density 23°C |
ISO 1183 |
1.03 |
g/cm³ |
| Shrinkage Flow 60x60x2mm |
ISO 294 |
0.4 |
% |
| Humidity Absorption 23°C 50RH Equilibrium |
ISO 62 |
0.3 |
% |
| Melt Index 220°C 10kg |
ISO 1133 |
19 |
cm³/10min |
| Hardness |
Standard |
Value |
Unit |
| Rockwell Hardness R(Scale) 23°C |
ISO 2039 |
110 |
| Mechanical behavior |
Standard |
Value |
Unit |
| Tensile Strength Yield 23°C 50mm/min |
ISO 527 |
48 |
Mpa |
| Tensile Strength Break 23°C 50mm/min |
ISO 527 |
37 |
Mpa |
| Elongation Break 23°C 50mm/min |
ISO 527 |
30 |
% |
| Flexural Strength Yield 23°C 2.0mm/min |
ISO 178 |
76 |
Mpa |
| Flexural Modulus 23°C 2.0mm/min |
ISO 178 |
2.2 |
Gpa |
| Izod Notch Impact 23°C |
ISO 180 |
19 |
kJ/m² |
| Charpy Notch Impact 23°C |
ISO 179 |
20 |
kJ/m² |
| Thermal |
Standard |
Value |
Unit |
|
Heat deflection temperature (HDT) Unannealed 1.8MPa
|
ISO 75
|
85
|
°C
|
|
Vicat Softening Temperature 50°C/hr 10N
|
ISO 306
|
102
|
°C
|
| Flammability |
Standard |
Value |
Unit |
|
Flame Rating All Color 1.5mm
|
UL94
|
HB
|
|
|
Flame Rating All Color 3.0mm
|
UL94
|
HB
|
|
| Injection molding |
Value |
Unit |
|
Dry Temperature
|
|
80~85
|
°C
|
|
Dry Time
|
|
2~4
|
hr
|
|
Zone1 Temperature
|
|
170~180
|
°C
|
|
Zone2 Temperature
|
|
185~215
|
°C
|
|
Zone3 Temperature
|
|
195~225
|
°C
|
|
Zone4 Temperature
|
|
185~215
|
°C
|
|
Nozzle Temperature
|
|
205~235
|
°C
|
|
Mould Temperature
|
|
40~70
|
°C
|
|
Injection Pressure
|
|
Moderate
|
|
|
Injection Speed
|
|
Moderate-Fast
|
|
|
Screw Speed
|
|
30~100
|
rpm
|
|
Back Pressure
|
|
50~70
|
psi
|
⚠️The technical data sheet (TDS) of Taitalac 5000W ABS, from Taita chemical company, if there are differences, please refer to the official website of Taitalac chemical.
Taitalac 5000W ABS Advantage
- Good processing conditions, Taitalac 5000W ABS material has a melt index of 19cm³/10min at 220℃ 10kg test environment, suitable for injection molding processing, and is very suitable for the production of complex and precise parts.
- Good appearance properties. Compared with conventional ABS materials, products made of Taitalac 5000W ABS materials have smooth surfaces and fewer defects, which has great advantages in application scenarios with more stringent requirements on appearance.
- Excellent high temperature resistance. Compared with conventional ABS materials, Taitalac 5000W ABS has a softening concentration of 102°C under a 50°C/hr 10N test environment. It can be used in office equipment, electronic and electrical equipment, and home appliance housings that require heat dissipation.
Why choose ATS as Taitalac 5000W ABS pellets supplier?
- Leading ABS (Acrylonitrile Butadiene Styrene) resin supplier, 10+ years of experience in plastic product manufacturing and chemical raw material import and export
- Fastest Arrival, with warehouses in multiple ports
- 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 10+ years
- Free Samples for production testing
- Wholesale price, even a piece of goods is based on the wholesale price
相关