Hopelex PC-1100 is a highly transparency polycarbonate resin (PC material) manufactured by Lotte Chemical, melt index (MFI) 10, containing flame retardant and release agent components, suitable for electrical applications, home appliance casings, and building materials
Key Attributes
| Lotte Hopelex PC-1100 PC pellets |
| Product information |
| Manufacturer |
Lotte chemical corporation |
|
Part Marking Code
|
>PC -FR<
|
|
Color
|
Transparent
|
|
Material Shape
|
PC Pellets
|
|
Process
|
·Injection molding grade PC pellets ·Extrusion molding grade PC pellets
|
|
Features
|
·Flame retardant ·Good mould release
|
|
Additives
|
·Flame retardant agent ·Mold releases
|
|
Application
|
·Complex parts ·Small parts
|
| Physical properties |
Standard |
Value |
Unit |
|
Density
|
ASTM D792
|
1.2
|
g/cm³
|
|
Shrinkage Flow
|
ASTM D955
|
0.5~0.7
|
%
|
|
Melt Index 300°C 1.2kg
|
ASTM D1238
|
10
|
g/10 min
|
| Mechanical behavior |
Standard |
Value |
Unit |
|
Tensile Strength Yield 50mm/min
|
ASTM D638
|
630
|
kg/㎡
|
|
Elongation Break 50mm/min
|
ASTM D638
|
100
|
%
|
|
Flexural Strength Yield 10mm/min
|
ASTM D790
|
920
|
kg/㎡
|
|
Flexural Modulus 10mm/min
|
ASTM D790
|
24000
|
kg/㎡
|
|
Izod Notch Impact 23°C 3.2mm
|
ASTM D256
|
80
|
kg-cm/cm
|
| Optical performance |
Standard |
Value |
Unit |
| Transmittance |
ASTM D1003 |
89 |
% |
| Haze |
ASTM D1003 |
0.8 |
% |
| Refractive Index |
ASTM D542 |
1.585 |
| Thermal |
Standard |
Value |
UnitH |
|
Heat deflection temperature (HDT) 0.45MPa
|
ASTM D648
|
143
|
℃
|
|
Heat deflection temperature (HDT) 1.58MPa
|
ASTM D648
|
132
|
℃
|
|
Vicat softending temperature 50℃/hr 50N
|
ASTM D1525
|
150
|
℃
|
| Flammability |
Standard |
Value |
Unit |
| Flame Rating NC 1.6mm |
UL94 |
V-2 |
| Flame Rating NC 3.2mm |
UL94 |
V-2 |
| Processing guides |
Standard |
Value |
Unit |
| Dry temperature |
120 |
℃ |
| Dry time |
4 |
hr |
| Maximum moisture content |
0.02 |
% |
| Melt temperature |
290-310 |
℃ |
| Nozzle temperature |
280-300 |
℃ |
| Barrel rear zone |
290-310 |
℃ |
| Barrel middle zone |
280-300 |
℃ |
| Barrel front zone |
270-290 |
℃ |
| Hopper temperature |
60-80 |
℃ |
| Mold temperature |
60-90 |
℃ |
⚠️The technical data sheet (TDS) of Lotte 1100 polycarbonate resin (PC material) from Lotte chemical, if there are differences, please refer to the official website of lotte.
Lotte PC-1100 PC Advantage
- Flame-retardant polycarbonate material, Lotte 1100 PC resin contains flame retardant components. Tested at a thickness of 1.6mm, its flame retardancy performance meets UL94 V-2 standards. It is suitable for appliance housings and heat dissipation modules requiring high flame retardancy and thermal management.
- High impact resistance, Lotte 1100 PC material exhibits a flexural modulus of 24,000 kgf/cm² at a test thickness of 10 mm/min and an Izod impact strength of 80 kg·cm/cm at a test environment of 23°C. It is suitable for products requiring high impact resistance, such as mechanical housings and appliance casings.
- Good machinability. PC Lotte 1100 exhibits a melt flow index (MFI or MVR) of 10g/10min under a 300°C, 1.2kg test environment. It is suitable for injection molding and extrusion processing methods, particularly for producing thin-walled products. Additionally, this material incorporates release agent components, facilitating large-scale rapid production.