Descripción
Product Features
| Tipo de Producto |
Raw Material |
Product Categories |
ASA |
CAS NO. |
71512-90-8 |
| Manufacturers |
LIHUAYI |
Grade |
6700 |
Appearance |
Natural |
| Packing Size |
25/KG Standard Packaging |
Import |
NO |
| Usage level |
Car Parts, Electronic Appliances |
| Feature level |
High Temperature Resistance |
| Processing Method |
Injection Molding |
Shape |
Particle |
Test Item | Test Method | Test Condition | Test Unit | Test Result |
Typical properties
|
Melt Flow Rate
|
ASTM D1238
|
220℃ 10kg
|
g/10min
|
6
|
|
Density
|
ISO 1183A
|
–
|
g/cm³
|
1.07
|
|
Tensile Strength
|
ASTM D638
|
3.2 mm,50mm/min
|
MPa
|
42
|
|
Tensile Modulus
|
ASTM D638
|
3.2 mm,1mm/min
|
MPa
|
2200
|
|
Flexural Strength
|
ASTM D790
|
3.2 mm,1.3mm/min
|
MPa
|
59
|
|
Flexural Modulus
|
ASTM D790
|
3.2 mm,1.3mm/min
|
MPa
|
1800
|
|
Izod Impact Strength
|
ASTM D256
|
3.5m/s
|
J/m
|
157
|
|
Izod Impact Strength
|
ISO 180
|
3.5m/s
|
kJ/m²
|
16
|
|
Heat Distortion Temperature
|
ASTM D648
|
1/4″ inch
|
℃
|
86
|
|
Heat Distortion Temperature
|
ISO 75
|
2+-0.2℃/min
|
℃
|
86
|
|
Rockwell Hardness
|
ASTM D785
|
23℃
|
R-scale
|
90
|
|
Vicat Softening Point
|
ASTM D1525
|
1/8″ inch
|
℃
|
98
|
|
Vicat Softening Point
|
ISO 306
|
50℃/h
|
℃
|
98
|
|
Molding Shrinkage
|
ASTM D955
|
3.2mm
|
%
|
0.4-0.7
|
|
Molding Shrinkage
|
ISO 2577
|
3.2mm
|
%
|
0.4-0.7
|