Celanese Celcon M90 POM pellet Description
Celcon M90 is a Polyformaldehyde resin (POM-C material) produced by Celanese. M90 POM material has a melt index of 8 cm³/10 min (at 190°C, 2.16 kg), medium viscosity, and offers good processing properties. can be processed in blow molding and extrusion molding processing methods, and has advantages in thin-walled products and pipe manufacturing.
Key Attributes
| Celanese Celcon M90 POM |
| Product information |
| Manufacturer |
Celanese Corporation |
| Part Marking Code |
>POM material< |
| Material Shape |
POM Pellets |
| Poymer |
Copolymer |
| Flame retardant |
HB |
| specification |
UL |
| Physical properties |
Standard |
Value |
Unit |
| Density |
ISO 1183 |
1410 |
kg/m³ |
| Shrinkage Flow |
ISO 294 |
2.0 |
% |
| Shrinkage ×Flow |
ISO 294 |
1.9 |
% |
| Water absorption 23℃ 24hr |
ISO 62 |
0.75 |
% |
| Water absorption 23℃ 50RH |
ISO 62 |
0.2 |
% |
| Melt Index 190℃ 2.16kg |
ISO 1133 |
8 |
cm³/10min |
| Mechanical behavior |
Standard |
Value |
Unit |
| Tensile Moudulus 23℃ |
ISO 527 |
2760 |
Mpa |
| Tensile strength 23℃ |
ISO 527 |
66 |
Mpa |
| Elongation 23℃ |
ISO 527 |
10 |
% |
| Tensile creep modulus 1hr |
ISO 899 |
2450
|
Mpa |
| Tensile creep modulus 1000hr |
ISO 899 |
1350 |
Mpa |
| Flexural modulus 23℃ |
ISO 178 |
2550 |
Mpa |
| Izod Notch impact 23℃ |
ISO 180 |
5.7 |
kJ/㎡ |
| Charpy notch impact 23℃ |
ISO 179 |
6 |
kJ/㎡ |
| Charpy notch impact -30℃ |
ISO 179 |
6 |
kJ/㎡ |
| Charpy un-notch impact 23℃ |
ISO 179 |
190 |
kJ/㎡ |
| Charpy un-notch impact -30℃ |
ISO 179 |
180 |
kJ/㎡ |
| Thermal |
Standard |
Value |
Unit |
| Heat deflection temperature (HDT) Unannealed 0.45Mpa |
ISO 75 |
158 |
°C |
| Heat deflection temperature (HDT) Unannealed 1.8Mpa |
ISO 75 |
101 |
°C |
| Melting temperature |
ISO 11357 |
165 |
℃ |
| CLE Flow |
ISO 11359 |
1.2E-4 |
cm/cm/℃ |
| CLE xFlow |
ISO 11359 |
1.2E-4 |
cm/cm/℃ |
| Flammability |
Standard |
Value |
Unit |
| Flame rating all color 0.71mm |
UL94 |
HB |
| Flame rating all color 1.5mm |
UL94 |
HB |
| Flame rating all color 3.0mm |
UL94 |
HB |
| Flame rating all color 6.0mm |
UL94 |
HB |
⚠️The technical data sheet (TDS) of Celanese Celclon M90 copolymer polyacetal resin (POM-C material) from Celanese, if there are differences, please refer to the official website of Celanese.
Celanese Celcon M90 POM pellets Advantage
- Easy to process, M90 POM exhibits a melt flow index (MFI or MVR) of 8 cm³/10 min at 190°C under a 2.16 kg test environment. It is suitable for injection molding and extrusion processing methods. The melt possesses medium viscosity and offers favorable processing conditions, making it compatible with the vast majority of production equipment. The material demonstrates strong machine adaptability.
-
Enhanced high-temperature resistance. Compared to homopolymer POM resin (POM-H material), Celcon M90 POM employs a copolymer POM processing method, offering superior high-temperature resistance. Its heat deflection temperature reaches 158°C under a 0.45MPa test environment, slightly exceeding that of POM-H. M90 POM is suitable for the production of components requiring long-term high-temperature resistance, such as bearings, chemical pump valves, and automotive trim parts.
-
Wide range of applications. Celcon M90 POM material, as an exceptionally versatile resin, is suitable for a wide range of applications including extruded profiles, automotive components, bearings, and precision gears.
Why choose ATS as Celanese Celcon M90 pellets supplier?