描述
LG HI-121H ABS Description
LG HI121 is a high rigidity,high impact resistant Acrylonitrile Butadiene Styrene (ABS material) with a melt index of 22g/10min (at 220°C, 10kg). It is easy to process and form, suitable for injection molding, can be used to produce toys, helmets, home appliance housings, pipes, and electronic and electrical applications.
Key Attributes
| LG HI-121H ABS |
| Product information |
| Manufacturer |
LG CHEM LTD. |
| Part Marking Code |
>ABS material< |
| Color |
Natural color |
| Material Shape |
ABS Pellets |
| Process |
Injection molding ABS material |
| Flame retardant |
HB |
| Material Attribute |
Injection grade ABS pellets |
| specification |
UL |
| Features |
·Good mechanical properties ·High stiffness |
| Application |
·E & E Applications ·Toys ·Safety helmet ·Washing machine ·Pipe ·Vacuum cleaners |
| UL File NO. |
67171 |
| Physical properties |
Standard |
Value |
Unit |
| Density 23°C |
ASTM D792 |
1.05 |
g/cm³ |
| Shrinkage 3.2mm 23℃ |
ASTM D955 |
0.4~0.7 |
% |
| Melt Index 220°C 10kg |
ASTM D1238 |
22 |
g/cm³ |
| Hardness |
Standard |
Value |
Unit |
| Rockwell Hardness R(Scale) |
ASTM D785 |
110 |
|
| Mechanical behavior |
Standard |
Value |
Unit |
| Tensile Modulus 23°C 50mm/min 3.2mm |
ASTM D638 |
2350 |
Mpa |
| Tensile Strength Yield 23°C 50mm/min 3.2mm |
ASTM D638 |
49 |
Mpa |
| Elongation Yield 23°C 50mm/min 3.2mm |
ASTM D638 |
5 |
% |
| Elongation Break 23°C 50mm/min 3.2mm |
ASTM D638 |
10 |
% |
| Flexural Strength 23°C 15mm/min 3.2mm |
ASTM D790 |
78 |
Mpa |
| Flexural Modulus 23°C 15mm/min 3.2mm |
ASTM D790 |
2550 |
Mpa |
| Izod Notch Impact 23°C 3.2mm |
ASTM D256 |
220 |
J/m |
| Izod Notch Impact -30°C 3.2mm |
ASTM D256 |
90 |
J/m |
| Izod Notch Impact 23°C 6.4mm |
ASTM D256 |
220 |
J/m |
| Izod Notch Impact -30°C 6.4mm |
ASTM D256 |
90 |
J/m |
| Thermal |
Standard |
Value |
Unit |
| HDT Unannealed 1.8MPa 6.4mm |
ASTM D648 |
85 |
°C |
| Vicat Softening Temperature 50°C/hr 50N |
ASTM D1525 |
92 |
°C |
| Flammability |
Standard |
Value |
Unit |
| Flame Rating All Color 1.5mm |
UL94 |
HB |
|
| Flame Rating All Color 3.0mm |
UL94 |
HB |
|
⚠️The technical data sheet (TDS) of LG HI121H ABS material, from LG chemical, if there are differences, please refer to the official websit of LG chemical.
LG HI-121H ABS Advantage
-
High rigidity ABS material. LG HI121H ABS has a cantilever beam notch impact of 220J/m at 3.2mm and 23℃ test environment, and can reach 90J/m even in extreme low temperature environment of -30℃. It is very suitable for applications with high impact resistance requirements, such as helmets, home appliance housings, toys, etc.
- Good processing performance. The melt index of LG HI121H ABS material under the 220℃ 10kg test standard is 22g/10min. It is suitable for injection molding processing. The requirements for processing equipment are relatively broad. The processing temperature window is large, the fault tolerance is high, and the finished product is stable and not easy to deform.
Why choose ATS as LG HI-121H ABS pellets supplier?
- Leading Acrylonitrile Butadiene Styrene resin pellet (ABS pellet) supplier, 10+ years of experience in plastic product manufacturing and chemical raw material import and export
- Fastest Arrival, with warehouses in multiple ports
- 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 10+ years
- Free Samples for production testing
- Wholesale price, even a piece of goods is based on the wholesale price
|
We have established long-term relationships with 80+ well-known companies around the world
|
Warehouse And Shipping
|
10+ years’ experience consultant with a supply chain of 1000+ plastic raw materials in China.
|
|
Quantity (tonnes)
|
1-100
|
100-300
|
>300
|
|
Lead time (days)
|
7-10
|
10-15
|
To be negotiate
|
相关